Specification ASTM D includes test methods for covering a wide range of mechanical properties of coated fabrics. ASTM D is used to ensure the quality of rubber-coated fabrics including tarpaulins, rainwear, outdoor clothing, and similar products. ASTM D features . 9 Sep This standard is issued under the fixed designation D ; the 1 These test methods are under the jurisdiction of ASTM Committee D11 on.

Author: Vujin Akizil
Country: Norway
Language: English (Spanish)
Genre: Sex
Published (Last): 3 January 2004
Pages: 131
PDF File Size: 6.16 Mb
ePub File Size: 7.38 Mb
ISBN: 719-6-28232-527-7
Downloads: 6954
Price: Free* [*Free Regsitration Required]
Uploader: Moogull

Five specimens should be cut with the smallest dimension at least A UTM and vise ast with the same 1×1 and 1×2 inserts are used. The long term increases in productivity and efficiency out-weigh the initial cost. Waterproof textiles are also usually tested to one or more of these standards.

Specimens should be rectangular in shape and 75mm X mm in size. Next run the test machine so that it separates the coating from the backing with a uniform speed of. XyLive Software allows you to asm the ashm live as the test runs. The oven only cycles heat, the samples should not be exposed to light. Preparing the Specimens for the Tongue Tear Method Five specimens from each of the warp and filling directions should be tested.

Testing Procedure Clamp the specialized fixture device in the upper clamp of the test machine and adjust the machine to compensate for its weight. We are happy to help! Pneumatic actuation allows for quick and simple d715 setup. This test determines the elongation of the coated fabric during the breaking strength tests.

ASTM D – 00 Standard Test Methods for Coated Fabrics

The other part of the fixture is a polished steel ball that is mounted to the top of the machine which is used to burst the fabric. The Tack-Tear test fixture is described in scant detail in the official publication. Procedure A is the preferred method to test, but Procedure B is also acceptable. Preparing the Specimens Create two sets of five specimens each for warp and filling tack-tear strength.

A rising water column tester is a simpler device compared to the Mullens tester. A tensile tester and vise grips with 2×3″ HxW grip inserts are used. ADMET universal testing machines include the straining mechanism item 1 and built in load and elongation recording mechanisms Item 3. We are confident that we have what you are looking for.

Small wick sized samples are put into a beaker with a water soluble dye. This test is characterized by a spherical plunger fixture. The specimen is then torn by the fall of a pendulum through the force of gravity.

ASTM D751 Coated Fabric Tensile Testing

Blocking resistance is tested by folding a piece of fabric sample a couple of times and then placing it in between two glass plates. Preparing the Specimens Use the same specimens as for breaking strength.

Specimens should be in rectangle shapes and should be 50mm W X mm L with the seam horizontally across the center. The other method, the Tongue Tear Method is more common and requires a universal testing machine.

Rated to 8 kN 1, lbf Clamping force up to 16 kN 3, lbf Maximum specimen thicknesses from 10 mm to 30 mm 0. Tack-Tear Resistance The Tack-Tear test fixture is described in scant detail in the official publication.

This test should be performed at the same time as breaking strength with the same specimens. This test determines the puncture resistance of the coated fabric.

The samples are then unfolded and allowed to reach more normal temperatures. Tack-tear fixture Crush resistance test fixture. Next impinge the specimen on the needles. Bursting Strength This s751 holds a piece of fabric securely on ast, top and bottom surface an exposed a circular area of fabric. Low Temperature Crack Resistance Crack resistance is tested at low temperature by means of a chilling chamber.

Tests include breaking strength by Procedure A: The literature recognizes rubber-coated fabrics, however the coverage is not limited to rubber, and extends to similar types of polymer coatings on textiles.

Breaking Strength — Procedure A: Specification ASTM D includes test methods for covering a wide range of mechanical properties of coated fabrics. Adhesion of coating shall be the average of the 5 highest peak loads during the test.

Dead Load Seam Strength is similar to the seam strength test. Place the load button on the test specimen with the recessed end down and at least 12 mm from any edge of the specimen.

Testing Procedure First clamp the separated portions of your sample in the jaws so that movement of the test machine will separate the coating from the backing. This special crush resistance fixture is unique to this test. The button has space to puncture through the sample. Wicking of Coated Cloth. Low Temperature Bend Test. This will be recorded by the UTM controller.